Bead Wire
| Price : | Price Negotiable |
| Quantity : | 300000 (metric ton) |
| Minimum Order : | 25 |
| Product Status : | New |
| Sample Available : | yes |
| Shipment Terms : | fob,cfr,cif |
| Payment Mode : |
T/T,L/C,cash |
| Categories : | Metallurgy, Mineral & Energy, Steel & Products |
| Posted By : | Weifang Senyu Trading Co., Ltd. |
Description
Brief introduction
As the important reinforcement of the tyres, made of steel and coated with copper, bead wire can strengthen the tyres.
Specification: We can offer bead wire mainly from Ф 0.89mm to Ф 1.65mm.
Packing: Packed in reels, and then put on pallets, using standard packing materials and methods. One 20' FCL container can hold 25 metric tons.
Payment terms: L/C at sight or T/T.
Specifications of Bead Wire:
Specification: Ф0.89
| Diameter（mm） | 0.89± 0.02 mm | |
| Breaking Strength（Kg/wire） | ≥115 | |
| Elongation (%) | ≥5% | |
| Torsion (Turns/L=200D) | ≥52 | |
| Straightness (mm/ 3m ) | ≤ 600 mm | |
| Bronze plate composition | ||
| Copper (%) | ≥97% | |
| Tin (%) | ≤3.0% | |
| Plating thickness (g/kg) | 0.30-1.35 | |
| Adhesion force (N) | ≥800N | |
| Tensile strength (Mpa) | ≥1850 Mpa | |
|
Steel Analysis | C (%) | 0.65-0.90 |
| Mn (%) | 0.30-0.80 | |
| Si (%) | 0.17-0.37 | |
| P&S (%) | ≤0.030 | |
| Linear Density (g/m) | 4.90±0.1 | |
| Bend on 2.50mm (Min) | 11 | |
Specification: Ф0.95
| Diameter（mm） | 0.95± 0.02 mm | |
| Breaking Strength（Kg/wire） | ≥136 | |
| Elongation (%) | ≥5% | |
| Torsion (Turns/L=200D) | ≥50 | |
| Straightness (mm/ 3m ) | ≤ 600 mm | |
| Bronze plate composition | ||
| Copper (%) | ≥97% | |
| Tin (%) | ≤3.0% | |
| Plating thickness (g/kg) | 0.30-1.35 | |
| Adhesion force (N) | ≥800N | |
| Tensile strength (Mpa) | ≥1850 Mpa | |
|
Steel Analysis | C (%) | 0.65-0.90 |
| Mn (%) | 0.30-0.80 | |
| Si (%) | 0.17-0.37 | |
| P&S (%) | ≤0.030 | |
| Linear Density (g/m) | 5.65±0.2 | |
| Bend on 2.50mm (Min) | 11 | |
Specification: Ф0.96
| Diameter（mm） | 0.96± 0.02 mm | |
| Appearance Quality | Appearance plating uniform and Qualified | |
| Tensile strength（Mpa） | ≥1850 | |
| Breaking Strength（Kg/wire） | ≥136 | |
| Elongation (%) | ≥5% | |
| Torsion (Turns/L=200D) | ≥50 | |
| Straightness (mm/ 3m ) | ≤ 600 mm | |
| Bronze plate composition | ||
| Copper (%) | ≥97% | |
| Tin (%) | ≤3.0% | |
| Plating thickness (g/kg) | 0.30-1.35 | |
| Adhesion force (N) | ≥800N | |
| Tensile strength (Mpa) | ≥1850 Mpa | |
|
Steel Analysis | C (%) | 0.65-0.90 |
| Mn (%) | 0.30-0.80 | |
| Si (%) | 0.17-0.37 | |
| P&S (%) | ≤0.030 | |
| Linear Density (g/m) | 5.68±0.2 | |
| Bend on 2.50mm (Min) | 11 | |
Specification: Ф1.0
| Diameter（mm） | 1.0± 0.02 mm | |
| Breaking Strength（Kg/wire） | ≥148 | |
| Elongation (%) | ≥5% | |
| Torsion (Turns/L=200D) | ≥52 | |
| Straightness (mm/ 3m ) | ≤ 600 mm | |
| Bronze plate composition | ||
| Copper (%) | ≥97% | |
| Tin (%) | ≤3.0% | |
| Plating thickness (g/kg) | 0.30-1.35 | |
| Adhesion force (N) | ≥800N | |
| Tensile strength (Mpa) | ≥1850 Mpa | |
|
Steel Analysis | C (%) | 0.65-0.90 |
| Mn (%) | 0.30-0.80 | |
| Si (%) | 0.17-0.37 | |
| P&S (%) | ≤0.030 | |
| Linear Density (g/m) | 6.20±0.2 | |
| Bend on 2.50mm (Min) | 11 | |
Specification: Ф1.65
| Diameter（mm） | 1.65± 0.03 mm | |
| Breaking Strength（Kg/wire） | ≥375 | |
| Elongation (%) | ≥5% | |
| Torsion (Turns/L=200D) | ≥40 | |
| Straightness (mm/ 3m ) | ≤ 600 mm | |
| Bronze plate composition | ||
| Copper (%) | ≥97% | |
| Tin (%) | ≤3.0% | |
| Plating thickness (g/kg) | 0.30-1.35 | |
| Adhesion force (N) | ≥800N | |
| Tensile strength (Mpa) | ≥1770Mpa | |
|
Steel Analysis | C (%) | 0.65-0.90 |
| Mn (%) | 0.30-0.80 | |
| Si (%) | 0.17-0.37 | |
| P&S (%) | ≤0.030 | |
| Linear Density (g/m) | 16.8±0.4 | |
| Bend on 2.50mm (Min) | 10 | |
Note: All the above products can be produced according to customers' requirements.
 |
|